We Joglekar Refractories Private Limited are the leading manufacturer of
Basic Ramming Mass, made from Dead Burnt Magnesite clinker in
association with Chromite Sand. Basic Ramming Mass is used as a
refractory material for lining of induction furnaces to withstand very
high temperatures. Ramming Mass is manufactured with great precision
using modern techniques and quality raw materials which is being
imported. Corrosion resistant with a high level of thermal stability, it
offers maximum output and last longer.
Our Signature Ramming Mass used in induction furnace for Basic Lining
|
|
Product Description
material made from Dead Burnt Magnesite clinker in association with
Chrome. Specially bonded with clays and other chemical binders to
achieve the desired sintering characteristics
Product Specification
MgO - 70% min, Cr2O3 - 8min, SiO2 - 8%max, CaO - 2% max
Sieve Distribution 0-4 and 0-5 mm
Send Enquiry
|
| |
|
|
 |
Ramming Mass named as Indspinel TA is made from Dead Burnt Magnesite clinker in association with Alumina. Ramming Mass is used as a refractory material for lining of induction furnaces to withstand very high temperatures. Ramming Mass is manufactured with great precision using modern techniques and quality raw materials which is being imported. Corrosion resistant with a high level of thermal stability, it offers maximum output and last longer.
Our Signature Ramming Mass used in induction furnace for Basic Lining
|
|
Product Description
An Induction furnace ramming material made from Dead Burnt Magnesite
clinker in association with Alumina. Specially bonded with clays and
other chemical binders to achieve the desired sintering characteristics.
Product Specification
MgO - 74% min, SiO2 - 6%max, Al2O3 - 14% min, CaO - 2%max
Sieve Distribution 0-4 and 0-5 mm
Send Enquiry
|
| |
|
|
 |
Neutral Ramming Mass named as Indspinel N is made from High performance Alumina clinker in association with Dead Burnt Magnesite. Neutral Ramming Mass is used as a refractory material for lining of induction furnaces to withstand very high temperatures. Ramming Mass is manufactured with great precision using modern techniques and quality raw materials which is being imported. Corrosion resistant with a high level of thermal stability, it offers maximum output and last longer.
Our Signature Ramming Mass Product used in Induction Furnace for lining.
|
|
Product Description
An Induction furnace ramming material made from Dead Burnt Magnesite and
Alumina. Specially bonded with clays and other chemical binders to
achieve the desired sintering characteristics.
Product Specification
Al2O3 - 84% min, MgO- 13% min, SiO2 - 2% max, CaO - 0.5% Max
Sieve Distribution 0-3mm
Send Enquiry
|
| |
|
 |
Ramming Mass named as Indspinel M is made from Dead Burnt Magnesite only. Ramming Mass is used as a refractory material for lining of induction furnaces to withstand very high temperatures. Ramming Mass is manufactured with great precision using modern techniques and quality raw materials which is being imported. Corrosion resistant with a high level of thermal stability, it offers maximum output and last longer.
Our Signature Ramming Mass used in induction furnace for
Basic Lining
|
|
Product Description
An Induction furnace ramming material made from Dead
Burnt Magnesite clinker in association with Special
Binders. It is bonded with clays and other chemical
binders to achieve the desired sintering
characteristics.
Product Specification
MgO - 86% Min.
Size - 0-4mm
Send Enquiry
|
|
| |
 |
Product Description
This material is designed for
repairing the cracks and other erosion that occurs in the lining during
usage. It possesses good workability and has no shrinkage upto
1650°C and has good erosion resisting properties. The chemical
composition is similar to the ramming mass but the grading/ binder is
different for good workability.
Product Specification
MgO - 68%, Cr2O3 - 8.8%, SiO2 - 10.5%, CaO -1.7%
Send Enquiry
|
 |
Product Description
This material is designed for repairing the cracks and other erosion
that occurs in the lining during usage. It possesses good workability
and has no shrinkage upto 1650 ° C and has good erosion resisting
properties. The chemical composition is similar to the ramming mass but
the grading/ binder is different for good workability..
Product Specification
MgO - 80% min, CaO - 1%min, Al2O3 - 10%max, SiO2 - 2%max,
Size 0-1mm
Send Enquiry
|
 |
Product Description
This material is designed for repairing the cracks and other erosion
that
occurs in the lining during usage. It possesses good workability and has
no
shrinkage upto 1650 °C and has good erosion resisting properties.
The
chemical composition is similar to the ramming mass but the grading/
binder
is different for good workability
iProduct Specification
AL2O3 - 72% Min., MgO - 24% Min., SiO2 - 2% max
Send Enquiry
|
| |
|
|
Product Description
This material is designed for repairing the cracks
and other erosion that occurs in the lining during usage. It possesses
good
workability and has no shrinkage upto 1650 °C and has good erosion
resisting
properties. The chemical composition is similar to the ramming mass but
the
grading/ binder is different for good workability.
Product Specification
MgO - 87 - 90%, SiO2 - 7-9%, Sieve distribution 0-1 mm
Send Enquiry
|
| |
|
|
 |
| |
|
| |
|
 |
It is used for making top on the induction furnace.
Product Description
MgO based formulation to be used with 8 to 10 % foundry grade Sodium
Silicate for making the area of furnace outside the coil and mouth of
furnace. Product has good resistance to wear due to mechanical abrasion.
Product Specification
MgO - 70%, Cr2O3 - 8%, SiO2 - 8%
Send Enquiry
|
 |
Used for Coating of the coil
Product Description
This is a High MgO based refractory powder blended with suitable binders
to protect the Induction furnace coils
Product Specification
MgO 84%, SiO2 9.5%, CaO 1.8%
Send Enquiry
|
| |
|
|
Can be used as a lining material for Ladles/ Hand shank (20 kg up to
1000 Kg. Capacity).
Product Description
This is Dunite based ramming mass with high refractoriness. It is having
high Specific Gravity and is resistant to slag. Ladles/hand shank lined
with Dutest-R gives much more life than ordinary materials thussaving
man-hours and improves the performance of the same.
Product Specification
MgO - 48% min; SiO2 - 40% max; Fe2O3 -10% max; Grading 0 - 4 mm
Service Temp. : 1700 °C, Sintering Temp: 800 °C
Send Enquiry
|
| |
|
 |
It helps to remove slag from iron and steel during the melting process.
Product Description
JRPL Slag Well (slag 30) is the best product to remove slag from iron
and steel when it melts in the Induction Furnace or Electric Arc
Furnace.
Product Specification
SiO2 -74%, Al2O3 -10%, MgO - 5%, CaO - 2%, Fe2O3 - 4%
Send Enquiry
|
| |
 |
 |
It is used for laying and repairing masonry construction of electric
furnace.
Product Description
It is used for laying and repairing magnesite brick, magnesite chrome
brick, magnesite alumina brick masonry construction of electric furnace.
Product Specification
MgO 60% min, SiO2 6%max, CaO 2%max, Cr2O3 13%
Send Enquiry
|
| |
|
 |
Product Description
ARC Ram is a pure magnesite based material and it is been
used in Electric ARC furnace for lining purpose.
Product Specification
Mgo 82-85%, SiO2 7-9%, CaO 1-3% Sieve distribution 0-4 mm